Eco-Friendly Copper Scrap Wire 99% Purity with Large Inventory for Recycling

Eco-Friendly Copper Scrap Wire 99% Purity with Large Inventory for Recycling

Product Parameters

Copper Wire

Item

Standard

Cu

≥99.99

As

≤0.0015

Sb

≤0.0015

Bi

≤0.0005

Fe

≤0.0025

Pb

≤0.0025

Sn

≤0.002

Ni

≤0.001

Zn

≤0.002

S

≤0.0025

P

≤0.001

Mechanical Properties: Our premium Eco-Friendly Copper Scrap Wire boasts impressive mechanical attributes. With a tensile strength of no less than 315 MPa and an elongation capacity of at least 30%, this product is engineered for performance.

Note: The described tensile mechanical properties are applicable to wires utilized at room temperature, with the exception of those specifically designed for crafting locks and clocks.

Sample Size & Temperature Specifications: The sample diameter ranges from greater than 2.0 to 4.0 mm. Our heat treatment standards specify a hot working temperature between 650 to 850ºC, paired with precise annealing temperature guidelines to ensure quality. Annealing Details: For low temperature annealing aimed at stress relief, the temperature range is set between 270 to 300ºC, while standard annealing processes occur between 600 to 700ºC to ensure optimal results.

Copper wire scrap, (Millberry) 99.99% at a purity of 99.98% min. 99.99%

Copper Wire Scrap

grade 1 copper scrap not mixed with specification C11000 Electrolytic tough pitch Berry Copper (ETP) Content 99.9%.

Cu%: 99.9%

Element...0.005... (%)

Copper..99.99... % (Min.)

Lead...0.005.... % (Max.)

Bismuth...0.5.. % (Max.)

Total impurities...0.3.. % (Max.)

Copper No. 2 kinds of alloy Wire cooper without lines, containing impurity, contain Copper quantity for 96% (minimum content 94%).

Shall not contain excessive lead and tin change of copper wire, welding of copper, brass and bronze line, excessive oil, prohibition and nonmetal,crisp, burning line, utterly margin of fine copper and excessive sexual yarn. Need appropriate means to remove dirt. Birch

Shall consist of clean, untinned, uncoated, unalloyed

copper wire and cable, not smaller than No. 16 B & S

wire gauge, free of burnt wire which is brittle

Pure copper scrap 99.99%

1.Copper wire scrap

2.Copper wire,tube,plate,etc

3.High quality:99%

Copper Scrap 99%

High-quality cable scrap with almost no impurities

Single Crystal Copper Wire

1.pure copper scrap

2.Good fatigue/abrasion/corrosion resistance

3.Be the bearing,switch,frame

Millberry Cu 99.9%min

Wire diameter: 0.30mm, 0.25mm, 0.20mm

competitive price.

Copper Scrap 99.9%

Specification:

Copper WIRE SCRAP, (Millberry) 99.99% at a purity of 99.98% min. 99.99% Max.

COPPER: 99.9%

CARBON: 0.03%

COBLET: <0.001

IRON: 0.005%

PHOSPHORUS: <.01%

SULPHUR: <.01%

ZINC: 0.003%

Zinc: 0.003%

High-purity Copper Wire Scrap (commonly labeled as Millberry) is defined by a minimum 99.9% copper content, often reaching 99.99% purity. It consists of clean, untinned, uncoated, unalloyed, and unburnt wire, usually 1.6mm or thicker, typically packed in 50kg bales or 1000kg bundles for electrical, melting, and recycling industries.

Key Technical Specifications (Millberry Grade)

Purity (Cu Content):

to

Appearance: Bright, clean, bare, stripped, uncoated

Composition:

Carbon:

Cobalt (Coblet):

Iron:

Phosphorus:

Sulphur:

Zinc:

Diameter: Common ranges are 0.20mm - 3mm (specifically 0.20, 0.25, 0.30mm for some specialized scrap)

Packaging: Bales (50kg), bundles (1000kg), or shrink-wrapped on pallets

Applications: Recycling into cathode, electrical components, high-grade alloys

Standard Grades (ISRI Classifications)

Bare Bright: Clean, unalloyed, uncoated, untinned copper wire, not burnt.

No. 1 Copper: Clean, unalloyed copper wire, pipe, or tubing, free of hair wire.

No. 2 Copper: Miscellaneous, unalloyed copper with a nominal 96% copper content (may contain solder, oxidized, or burnt wire).

Physical Characteristics

Appearance: Bright, shiny red/golden color

Physical Shape: Wire, cable, or stripped conductors

Quality: Free of brittle burnt wire, excessive oils, and insulation

Bare Bright

Consists of clean, untinned, uncoated, unalloyed copper wire and cable, free of burnt wire. Wire gage subject to agreement between buyer and seller. Free of copper tubing.

Copper Wire Recycling

No. 1 Copper

Consists of clean, untinned, uncoated, unalloyed copper wire and cable, burnt wire, and clean copper tubing. Wire gage subject to agreement between buyer and seller.

Copper Recycling

No. 2 Copper

Consists of miscellaneous, unalloyed copper wire and tubing having a nominal 96% copper content. Excessively leaded tinned, soldered, copper wire, brass and bronze wire, excessive oil content, iron, and non-metallics, copper wire from burning, insulation, hair wire, brittle burnt wire, and should be reasonably free of ash.

Copper Recycling

No. 3 Copper

Consists of miscellaneous unalloyed copper scrap having a nominal 92% copper content. This includes sheet copper, gutters, kettles, boilers, downspouts and similar scrap.

Copper Recycling

Insulated Copper Wire

Consists of various types of insulation over copper wire. To be bought and sold on a recovery basis.

Copper Wire Recycling

Copper Bearing Scrap

Consists of miscellaneous copper-containing skimmings, grindings, ashes, irony brass and copper, residues, and slag. Shall be free of insulated wire, copper chlorides, and unprepared tangled material.

Brass Recycling

Yellow Brass

Contains a minimum of 60% copper and maximum 5% iron. Shall be free of insulated wire, grindings, electrotype shells and non-metallics.

Copper Recycling

Red Brass

Consists of red brass valves, machinery. Shall be free of semi-red brass castings. No piece to measure over 12” over any part or weigh more than 100 lbs.

Brass Recycling

Brass Clips

Consists of brass alloy stamping or sheet material. Purchase agreed by the buyer and seller based on the alloy type of the material.

Brass and Copper Recycling

Brass Turnings

Consists of scrap borings or turnings alloyed with copper, tin, bismuth, and zinc. Turnings shall be unmixed and less than 0.2% alloyed lead.

Brass Turnings Recycling

Brass Shells

Consists of clean fired 70/30 brass shell cases free of primers and any other foreign material. All shells must be sufficiently mutilated to prevent reuse and reloading.